LNP™ THERMOTUF™ OF006I compound
| Category: | PPS, Linear , Linear Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOTUF™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tnNR3y_LNP-THERMOTUF-OF006I-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOTUF* OF006I is a compound based on PPS - Linear resin containing Glass Fiber. Added features of this material include: High Impact. Also known as: LNP* THERMOTUF* Compound OF-1006 HI Product reorder name: OF006I |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.49 | g/cm³ | ASTM D792 |
| -- | 1.48 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.20 | % | ASTM D955 |
| Across Flow : 24 hr | 0.70 | % | ASTM D955 |
| Across Flow : 24 hr | 0.67 | % | ISO 294-4 |
| Flow : 24 hr | 0.23 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10800 | MPa | ASTM D638 |
| -- | 9820 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 143 | MPa | ASTM D638 |
| Break | 139 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.4 | % | ASTM D638 |
| Break | 2.0 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9790 | MPa | ASTM D790 |
| -- | 10100 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 208 | MPa | ASTM D790 |
| -- | 212 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 170 | J/m | ASTM D256 |
| 23°C 2 | 16 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 780 | J/m | ASTM D4812 |
| 23°C 3 | 51 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.4 | J | ASTM D3763 |
| -- | 4.89 | J | ISO 6603-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 to 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 304 to 316 | °C | |
| Middle Temperature | 321 to 332 | °C | |
| Front Temperature | 332 to 343 | °C | |
| Processing (Melt) Temp | 316 to 321 | °C | |
| Mold Temperature | 138 to 166 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Polyester TC 197 | Saudi Basic Industries Corporation (SABIC) | PET | SABIC® HDPE |
| Adsyl 5 C 33 F | LyondellBasell Industries | Polyolefin, Unspecified | Adsyl |
| BESTNYL SE30VI01AH | Triesa Plastics | Nylon 66 | BESTNYL |
| Cheng Yu NG1400S | Cheng Yu Plastic Company Limited | Nylon 66 | Cheng Yu |
| Sylvin 9604-90 White 1241 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |