LNP™ LUBRICOMP™ DBL32 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tnCX7y_LNP-LUBRICOMP-DBL32-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* DBL32 is a compound based on Polycarbonate resin containing 10% Glass Beads and 15% PTFE. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DBL-4032 Product reorder name: DBL32 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.70 to 0.90 | % | ASTM D955 |
| Across Flow : 24 hr | 0.90 to 1.1 | % | ASTM D955 |
| Across Flow : 24 hr | 0.96 | % | ISO 294-4 |
| Flow : 24 hr | 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2070 | MPa | ASTM D638 |
| -- | 2580 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 42.7 | MPa | ASTM D638 |
| Yield 2 | 42.0 | MPa | ASTM D638 |
| Yield | 43.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Break | 38.6 | MPa | ASTM D638 |
| Break 3 | 38.0 | MPa | ASTM D638 |
| Break | 38.0 | MPa | ISO 527-2, ISO 527-2/5 |
| Tensile Elongation | |||
| Yield | 5.4 | % | ASTM D638 |
| Yield 4 | 5.4 | % | ASTM D638 |
| Yield | 5.1 | % | ISO 527-2, ISO 527-2/5 |
| Break | 22 | % | ASTM D638 |
| Break 5 | 22 | % | ASTM D638 |
| Break | 18 | % | ISO 527-2, ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2750 | MPa | ASTM D790 |
| -- | 2760 | MPa | ASTM D790 |
| -- | 2400 | MPa | ISO 178 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Stress | 69.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.42 | ||
| vs. Itself - Static | 0.48 | ||
| Wear Factor - Washer | 139 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D256 |
| 23°C 8 | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1500 | J/m | ASTM D4812 |
| 23°C 9 | 110 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 31.5 | J | ASTM D3763 |
| -- | 25.8 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 135 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 5.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PVC VSL-4601-N | Sumitomo Bakelite Co., Ltd. | PVDC | SUMILITE® PVC |
| Nanjing Hongrui PA66 A1305 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Keltan® 6160D | LANXESS Buna GmbH | EPDM | Keltan® |
| HOPELEX PCG-2105 | Lotte Chemical Corporation | PC | HOPELEX |
| LinGen FR600 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP, Unspecified | LinGen |