DOWLEX™ 6001GC

Category:	LLDPE , Polyethylene Resin
Manufacturer:	The Dow Chemical Company
Trademark:	DOWLEX™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tn5NET_DOWLEX-6001GC.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

DOWLEX™ 6001GC Polyethylene Resin is an ethylene, 1-octene copolymer, suitable for high performance blown film applications alone or in blends with LDPE. It offers superior seal performance at high extrusion output rates and an excellent balance of optical and mechanical properties.
Main Characteristics:

Optimum extruder output and stability, pure or in blends.

Combination of sealability with optical and mechanical properties

Applications:

Lamination Films for Food and Specialty Packaging

Frozen Food Packaging

Fresh Food Packaging

Complies with:

Europe Commission Regulation (EU) No 10/2011EU

U.S. FDA FCN 424

Consult the regulations for complete details

General Information
Additive	Anti-caking agent (2500 ppm) Sliding agent (900 ppm)
Agency Ratings	FDA FCN 424 Europe 10/1/2011 12:00:00 AM
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.915	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/2.1 kg)	0.70	g/10 min	ASTM D1238

Films	Nominal Value	Unit	Test Method
Film Thickness - Tested	50	µm
Tensile Modulus			ISO 527-3
2% secant, MD : 50 µm	105	MPa	ISO 527-3
2% secant, TD : 50 µm	110	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 50 µm	5.20	MPa	ISO 527-3
TD : Yield, 50 µm	8.00	MPa	ISO 527-3
MD : Break, 50 µm	38.9	MPa	ISO 527-3
TD : Break, 50 µm	34.7	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Break, 50 µm	610	%	ISO 527-3
TD : Break, 50 µm	630	%	ISO 527-3
Dart Drop Impact (50 µm)	1100	g	ISO 7765-1/A
Elmendorf Tear Strength ¹			ASTM D1922
MD : 50 µm	830	g	ASTM D1922
TD : 50 µm	1100	g	ASTM D1922
Seal Initiation Temperature (50 µm)	96.0	°C	Internal method

Optical	Nominal Value	Unit	Test Method
Gloss (45°, 50.0 µm)	66		ASTM D2457
Haze (50.0 µm)	9.0	%	ASTM D1003

Extrusion instructions
Fabrication Conditions For Blown Film Extrusion: Melt Temperature: 220°C Die Diameter: 150 mm Die Gap: 1.5 mm Blow-Up Ratio: 2.5 Film Thickness: 50 µm.

Note Message
1 .	Method B

Resin Grade	Manufacturer	Category	Trademark
TECHNYL® C 216 V30 BLACK Z/4	Solvay Engineering Plastics	Nylon 6	TECHNYL® C
Axiall PVC 10705	Axiall Corporation	PVC, Flexible	Axiall PVC
ENFLEX V1025A BLK UV	ENPLAST Americas, a Ravago Group Company	TPV	ENFLEX
Haysite Plastics H232	Haysite Reinforced Plastics	Polyester, TS	Haysite Plastics
HIVOREX 6010BP	Lotte Chemical Corporation	HDPE	HIVOREX