VICTREX® PEEK 450CA30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tlbNt4_VICTREX-PEEK-450CA30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% carbon fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour black. Applications for higher strength and stiffness in a static or dynamic system. Excellent wear resistance, low coefficient of friction, low coefficient of thermal expansion. Chemically resistant to aggressive environments. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Vertical flow direction : 170°C, 3.00mm | 0.50 | % | |
| Flow direction : 170°C, 3.00mm | 0.10 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 25000 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 260 | MPa | ISO 527-2 |
| Fracture, 125°C | 160 | MPa | ISO 527-2 |
| Fracture, 175°C | 85.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 50.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 23000 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 380 | MPa | ISO 178 |
| 125°C | 250 | MPa | ISO 178 |
| 175°C | 120 | MPa | ISO 178 |
| 275°C | 60.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 300 | MPa | ISO 604 |
| 120°C | 200 | MPa | ISO 604 |
| 200°C | 70.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 9.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 45 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 336 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : < 143°C | 5.0E-6 | cm/cm/°C | ISO 11359-2 |
| Flow : > 143°C | 6.0E-6 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 4.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1800 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.95 | W/m/K | ISO 22007-4 |
| RTI Imp | 200 | °C | UL 746 |
| RTI | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 1(23°C) | 1.0E+5 | ohms·cm | ASTM D4496 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Toxicity | NES 713 | ||
| CO Content | 0.0500 | NES 713 | |
| CO2 Content | 0.120 | NES 713 | |
| Total Gases | 0.170 | NES 713 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 675 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 375 | °C | |
| Middle Temperature | 380 - 385 | °C | |
| Front Temperature | 390 | °C | |
| Nozzle Temperature | 395 | °C | |
| Mold Temperature | 180 - 210 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | 1V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arnite® XG 260 S (T-X07086) | DSM Engineering Plastics | PBT | Arnite® |
| OXNILON 6 50GF | Oxford Polymers | Nylon 6 | OXNILON 6 |
| Sumiliteresin® PR-50869B | SBHPP | Phenolic | Sumiliteresin® |
| Sylvin 9604-80 Blue 8441 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LEXAN™ OQ4120R resin | SABIC Innovative Plastics | PC | LEXAN™ |