TEDUR® L 9217-1
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | TEDUR® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tlVOax_TEDUR-L-9217-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TEDUR® L 9217-1 is a Polyphenylene Sulfide (PPS) product filled with 65% glass\mineral. It is available in Asia Pacific, Europe, or North America. Applications of TEDUR® L 9217-1 include automotive, engineering/industrial parts and lighting applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.97 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 19000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Flexural Modulus | 19000 | MPa | ISO 178 |
| Flexural Stress | 240 | MPa | ISO 178 |
| Flexural Strain at Flexural Strength | 1.4 | % | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Unnotched Izod Impact Strength | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 140 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 320 to 340 | °C | |
| Mold Temperature | > 140 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC6GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| DiaAlloy FC-35 | Mitsubishi Rayon America Inc. | PC | DiaAlloy |
| LNP™ THERMOCOMP™ UX04509 compound | SABIC Innovative Plastics | PPA | LNP™ THERMOCOMP™ |
| LTM® 317-1B | Cytec Industries Inc. | Epoxy | LTM® |
| PENTESTER BT H black | PENTAC Polymer GmbH | PBT | PENTESTER BT |