OmniPro™ HPP GMR40
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | OMNI Plastics, LLC |
| Trademark: | OmniPro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tlGNdF_OmniPro-HPP-GMR40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40% Glass/Mineral Reinforced, Chemically Coupled, Homopolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.18 mm) | 146 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 204 to 249 | °C | |
| Middle Temperature | 216 to 260 | °C | |
| Front Temperature | 216 to 260 | °C | |
| Nozzle Temperature | 216 to 260 | °C | |
| Processing (Melt) Temp | 216 to 260 | °C | |
| Mold Temperature | 26.7 to 60.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH3TF2-Natural | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Ateva® 1608 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Karina WHITE PVC COMPOUND 902-10/30-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POTICON AT342 | Otsuka Chemical Co., Ltd. | Acetal (POM) Copolymer | POTICON |
| Sylvin 6221-83 Orange 5119 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |