LNP™ THERMOCOMP™ DX07350 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tkvY5z_LNP-THERMOCOMP-DX07350-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN *DX07350 resin is a glass filled, Non-brominated & Non-chlorinated flame retardant polycarbonate. High stiffness and good flow. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.35 to 0.45 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.090 | % | |
| Equilibrium, 23°C, 50% RH | 0.050 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | ASTM D3363 | ||
| -- 1 | F | ||
| -- 2 | HB |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 3 | 4700 | MPa | ASTM D638 |
| -- | 4800 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 4 | 65.0 | MPa | ASTM D638 |
| Yield | 68.0 | MPa | ISO 527-2/5 |
| Break 5 | 55.0 | MPa | ASTM D638 |
| Break | 54.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 6 | 4.0 | % | ASTM D638 |
| Yield | 3.8 | % | ISO 527-2/5 |
| Break 7 | 5.0 | % | ASTM D638 |
| Break | 4.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 8 | 4200 | MPa | ASTM D790 |
| -- 9 | 4600 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 120 | MPa | ISO 178 |
| Yield, 50.0 mm Span 10 | 116 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 11 | ISO 179/1eA | ||
| -30°C | 3.3 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength 12 | ISO 179/1eU | ||
| -30°C | 61 | kJ/m² | |
| 23°C | 75 | kJ/m² | |
| Notched Izod Impact | |||
| -30°C | 35 | J/m | ASTM D256 |
| 23°C | 42 | J/m | ASTM D256 |
| -30°C 13 | 4.6 | kJ/m² | ISO 180/1A |
| 23°C 14 | 4.7 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 15 | ISO 180/1U | ||
| -30°C | 47 | kJ/m² | |
| 23°C | 50 | kJ/m² | |
| Instrumented Dart Impact (23°C, Total Energy) | 11.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 102 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 16 | 104 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 112 | °C | ASTM D1525, ISO 306/B120 13 17 |
| -- | 109 | °C | ISO 306/B50 |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.6E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm, Testing by SABIC) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 260 to 290 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 270 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 0.5 kgf |
| 2 . | 1 kgf |
| 3 . | 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | Type I, 5.0 mm/min |
| 7 . | Type I, 5.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 1.3 mm/min |
| 11 . | 80*10*3 sp=62mm |
| 12 . | 80*10*3 sp=62mm |
| 13 . | 80*10*3 |
| 14 . | 80*10*3 |
| 15 . | 80*10*3 |
| 16 . | 80*10*4 mm |
| 17 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoflon® FOR 7380K | Solvay Specialty Polymers | Fluorelastomer | Tecnoflon® |
| NEFTEKHIM PP 4240N (EP2YX29GA) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| EnCom PPE-PS 235-04 | EnCom, Inc. | PPE+PS | EnCom |
| Hostacom HBS831DC | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 4250-55 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |