Adsyl 6 C 30 F
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adsyl |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | timUyQ_Adsyl-6-C-30-F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adsyl 6 C 30 F is a new advanced polyolefin, specially designed for use as a sealing layer in co-extruded film applications. This grade features a very low seal initiation temperature (<100°C) and excellent optical properties. It does not contain slip or anti-block additives. For regulatory information please refer to Adsyl 6 C 30 F Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.5 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3/25 | ||
| MD : 50 µm, Cast Film | 260 | MPa | |
| TD : 50 µm, Cast Film | 250 | MPa | |
| Tensile Stress | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 14.0 | MPa | |
| TD : Yield, 50 µm, Cast Film | 14.0 | MPa | |
| MD : Break, 50 µm, Cast Film | 37.0 | MPa | |
| TD : Break, 50 µm, Cast Film | 41.0 | MPa | |
| Tensile Elongation | ISO 527-3/500 | ||
| MD : Yield, 50 µm, Cast Film | 16 | % | |
| TD : Yield, 50 µm, Cast Film | 14 | % | |
| TD : Break, 25 µm, Cast Film | 900 | % | |
| MD : Break, 50 µm, Cast Film | 850 | % | |
| Seal Initiation Temperature | 95.0 | °C |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 59.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 103 | °C | ISO 306/A50 |
| Melting Temperature | 128 | °C | ISO 11357-3 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Cast Film) | 92 | ASTM D2457 | |
| Haze (50.0 µm, Cast Film) | 0.20 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMALENE WPP541K | Southern Polymer, Inc. | LDPE | PRIMALENE |
| ICORENE® Foam Products | ICO Polymers NA, A Division of A. Schulman | PE, Unspecified | ICORENE® |
| I. Stern BLK100 | I. STERN & CO. INC. | PS (HIPS) | I. Stern |
| LUVOCOM® NSB 90 BK-2 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| POCAN® KU 2-7003 POS042 000000 | LANXESS GmbH | PBT | POCAN® |