Pro-fax 6329
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Pro-fax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tiLTWe_Pro-fax-6329.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pro-fax 6329 polypropylene homopolymer is available in pellet form. This resin is typically used in injection molding applications and offers good resistance to aging at elevated temperatures in both wet and dry environments. For regulatory compliance information see Pro-fax 6329 Product Stewardship Bulletin (PSB). |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792B |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 13 | % | ASTM D638 |
| Flexural Modulus - 1% Secant 2 | 1170 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 96.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 C | RTP Company | Nylon 11 | RTP |
| WELLAMID Nylon 6600 GS 40 HWCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| ACCUCOMP™ HP0315L | ACLO Compounders Inc. | PP Homopolymer | ACCUCOMP™ |
| Arnite® A-X07302 (AV2 390 XT-P) | DSM Engineering Plastics | PET | Arnite® |
| Lanufene HBD-5224 | Ras Lanuf Oil & Gas Processing Company (RASCO) | HDPE | Lanufene |