Lucky Enpla LGF3202F
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Lucky Enpla Co LTD |
| Trademark: | Lucky Enpla |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgUk4c_Lucky-Enpla-LGF3202F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lucky Enpla LGF3202F is a polybutene terephthalate (PBT) product, which contains a 20% glass fiber reinforced material. It can be processed by injection molding and is available in North America, Europe or the Asia-Pacific region. Lucky Enpla LGF3202F applications include electrical/electronic applications and the automotive industry. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 108 | MPa | ASTM D638 |
| Flexural Modulus 2 | 6670 | MPa | ASTM D790 |
| Flexural Strength 3 | 163 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (3.18 mm) | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 204 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 90.0 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 240 - 260 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Mold Temperature | 80.0 - 110 | °C | |
| Back Pressure | 0.490 - 2.94 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Injection instructions |
|---|
| Resin Temperature: 230-250°CInjection Pressure (1st Pressure): 600-1100 kg/cm²Injection Pressure (2nd Pressure): 400-800 kg/cm² |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 3.0 mm/min |
| 3 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| S&E PVC GF-1807 | S&E Specialty Polymers, LLC | PVC+NBR | S&E PVC |
| SLOVAMID® 6 LI/1 LS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Andur 9-5 APLF | Anderson Development Company | PUR-Ester/TDI | Andur |
| OnForce™ LFT NN-60LGF/000 HS UV Black | PolyOne Corporation | Nylon 66 | OnForce™ LFT |
| Plenco 04568 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |