Generic ASA+PC
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgUBZo_Generic-ASA-PC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic ASA+PC This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.10 - 1.25 | g/cm³ | ASTM D792 |
| 23°C | 1.11 - 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 260°C/5.0 kg | 14 - 45 | g/10 min | ASTM D1238 |
| 260°C/5.0 kg | 19 - 40 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 17.0 - 26.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.50 - 0.60 | % | ASTM D955 |
| 23°C | 0.59 - 0.70 | % | ISO 294-4 |
| Water Absorption | |||
| 23°C, 24 hr | 0.10 - 0.25 | % | ASTM D570 |
| Saturated, 23°C | 0.60 - 1.0 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 - 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (23°C) | 109 - 116 | ASTM D785 | |
| Ball Indentation Hardness | 88.7 - 110 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 2540 - 2720 | MPa | ASTM D638 |
| 23°C | 2120 - 2760 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 52.9 - 65.6 | MPa | ASTM D638 |
| Yield, 23°C | 54.6 - 62.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 44.0 - 66.0 | MPa | ASTM D638 |
| Fracture, 23°C | 39.0 - 64.3 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield, 23°C | 3.7 - 6.1 | % | ASTM D638 |
| Yield, 23°C | 2.3 - 8.7 | % | ISO 527-2 |
| Fracture, 23°C | 23 - 100 | % | ASTM D638 |
| Fracture, 23°C | 36 - 80 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 2080 - 2770 | MPa | ASTM D790 |
| 23°C | 2000 - 2640 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 68.0 - 94.0 | MPa | ASTM D790 |
| 23°C | 72.8 - 97.5 | MPa | ISO 178 |
| Yield, 23°C | 81.7 - 95.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 - 62 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 140 - 600 | J/m | ASTM D256 |
| 23°C | 16 - 61 | kJ/m² | ISO 180 |
| Instrumented Dart Impact (23°C) | 35.3 - 47.9 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 102 - 130 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 98.4 - 132 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 87.7 - 113 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 87.2 - 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 104 - 138 | °C | ASTM D1525 |
| -- | 102 - 139 | °C | ISO 306 |
| Linear thermal expansion coefficient | |||
| Flow | 7.2E-5 - 7.3E-5 | cm/cm/°C | ASTM E831 |
| Flow | 1.0E-5 - 8.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 7.2E-5 - 7.9E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 7.1E-5 - 7.8E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 - 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+13 - 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature | 550 - 960 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 78.8 - 120 | °C | |
| Drying Time | 3.0 - 3.6 | hr | |
| Suggested Max Moisture | 0.020 - 0.052 | % | |
| Suggested Shot Size | 55 - 60 | % | |
| Rear Temperature | 215 - 247 | °C | |
| Middle Temperature | 240 - 252 | °C | |
| Front Temperature | 250 - 260 | °C | |
| Nozzle Temperature | 240 - 255 | °C | |
| Processing (Melt) Temp | 249 - 281 | °C | |
| Mold Temperature | 60.0 - 80.7 | °C | |
| Back Pressure | 0.300 - 0.785 | MPa | |
| Screw Speed | 50 - 55 | rpm | |
| Vent Depth | 0.057 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic ASA+PCThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| COSMOTHENE® EVA KA-40 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® EVA |
| ISOTHANE® 5080A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyether | ISOTHANE® |
| LubriOne™ PC-30GF/15T BLACK | PolyOne Corporation | PC | LubriOne™ |
| PHOENIX™ 9981 | Phon Tech Industrial Company | TPE | PHOENIX™ |
| Cereplast Compostables® 1010 | Trellis Bioplastics | PLA | Cereplast Compostables® |