VITAMIDE® BR36GY6151
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tgGP7V_VITAMIDE-BR36GY6151.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® BR36GY6151 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.40 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.95 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 180 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.2 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8700 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 260 | MPa | ISO 178 |
| Break | 260 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength 1 | 24.0 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength | 24 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 215 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 205 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 220 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 7.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 22 | kV/mm | ASTM D149, IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Oxygen Index | 22 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE H 522 Y7 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Flontech® FT-1-FM-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| K-Resin® SBC BK10 | Chevron Phillips Chemical Company LLC | SBC | K-Resin® SBC |
| Hyosung Polyketone M230A | Hyosung Corporation | PK-Aliphatic | Hyosung Polyketone |
| LNP™ LUBRILOY™ DF2041 compound | SABIC Innovative Plastics | PC | LNP™ LUBRILOY™ |