Di-Pak™ R-4525/7
| Category: | TP, Unspecified , Thermoplastic |
| Manufacturer: | Hapco Inc. |
| Trademark: | Di-Pak™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tf6Dsd_Di-Pak-R-4525-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
RIGID DI-PAK R-4525 Series A general purpose series of low viscosity, strong, potting and encapsulating compounds. DI-PAK R-4525 has excellent electrical insulating properties and bonds well to many substrates. By varying the curing agents, the desired cure and working life can be obtained. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.51 | g/cm³ | ASTM D4669 |
| Molding Shrinkage - Flow | 0.050 to 0.20 | % | ASTM D2566 |
| Weight - per cubic inch | 25 | g |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | 155 | °C |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time 1(25°C) | 50.0 | min | ASTM D2971 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2740 | MPa | ASTM D638 |
| Tensile Strength | 62.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.1 | % | ASTM D638 |
| Flexural Modulus | 2770 | MPa | ASTM D790 |
| Flexural Strength | 69.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 24 | J/m | ASTM D256 |
| Unnotched Izod Impact | 35 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Conductivity | 0.43 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.6E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 1 kHz | 4.30 | ||
| 100 kHz | 4.20 | ||
| Dissipation Factor (25°C, 100 kHz) | 7.0E-3 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Part B | Mix Ratio by Weight: 13, Mix Ratio by Volume: 20 | ||
| Thermoset Mix Viscosity (25°C) | 12500 | cP | ASTM D4878 |
| Demold Time | |||
| 21°C | 960 to 1400 | min | |
| 66°C | 120 to 240 | min |
| Note Message | |
|---|---|
| 1 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRE-ELEC® CP 1316 | Premix Oy | Polyolefin, Unspecified | PRE-ELEC® |
| Santoprene™ 201-67W171 | ExxonMobil Chemical | TPV | Santoprene™ |
| Sarlink® TPV 24955N | Teknor Apex Company | TPE | Sarlink® TPV |
| Petrothene® GA502024 | LyondellBasell Industries | LLDPE | Petrothene® |
| Plaslube® PA6/6 GL10 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |