LNP™ STAT-KON™ Ultem_UC1200 compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tevEug_LNP-STAT-KON-Ultem-UC1200-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP STAT-KON ULTEM_UC1200 is a 12% carbon fiber reinforced PEI. High modulus with ESD characteristics for high-heat applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (337°C/6.6 kg) | 7.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.12 to 0.22 | % | |
| Across Flow : 3.20 mm | 0.30 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8140 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 131 | MPa | |
| Break | 131 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 5.1 | % | |
| Break | 5.1 | % | |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 4 | 7830 | MPa | |
| 100 mm Span 5 | 8270 | MPa | |
| Flexural Strength | ASTM D790 | ||
| Break, 50.0 mm Span 6 | 221 | MPa | |
| Break, 100 mm Span 7 | 193 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 420 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 6.21 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 213 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 209 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 210 | °C | |
| Vicat Softening Temperature | 214 | °C | ASTM D1525 8 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | |
| Flow : -20 to 150°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 3.2E-5 | cm/cm/°C | |
| Transverse : -20 to 150°C | 4.0E-5 | cm/cm/°C | |
| RTI Elec | 105 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI Str | 105 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 4.0E+2 | ohms·cm | ASTM D257 |
| High Amp Arc Ignition (HAI) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 | |
| Static Decay 9 | 10 | msec | FTMS 101B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.57 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Drying Time, Maximum | 24 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 360 to 404 | °C | |
| Middle Temperature | 371 to 421 | °C | |
| Front Temperature | 382 to 427 | °C | |
| Nozzle Temperature | 377 to 421 | °C | |
| Processing (Melt) Temp | 382 to 427 | °C | |
| Mold Temperature | 135 to 163 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.6 mm/min |
| 8 . | Rate B (120°C/h), Loading 2 (50 N) |
| 9 . | 5000V to <50V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-250 | SHIN-A T&C | Epoxy | SHIN-A |
| DIALAC® U407 | UMG ABS, Ltd. | MMBS | DIALAC® |
| DuPure® SU 76 A | Ducor Petrochemicals BV | PP Impact Copolymer | DuPure® |
| PLUSTEK PA310G8BK10 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |
| ULTEM™ 1285 resin | SABIC Innovative Plastics | PEI | ULTEM™ |