DENYL HT 2010 Y
| Category: | PPA+Nylon , Polyphthalamide + Nylon |
| Manufacturer: | Vamp Tech |
| Trademark: | DENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | terYaI_DENYL-HT-2010-Y.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPA/PA 66 20% glass fiber reinforced, good mechanicals properties, low water absorption, high chemical resistance and excellent operating temperature. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.45 | % | |
| Across Flow | 0.80 | % | |
| Water Absorption (Saturation) | 0.40 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7800 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.5 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 5.0 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 250 | °C | ASTM D648A |
| RTI Elec | 140 | °C | UL 746 |
| RTI Imp | 140 | °C | UL 746 |
| RTI Str | 140 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | ASTM D257 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 300 | °C | |
| Mold Temperature | 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TPUCO® TPUI-E85 | Taiwan PU Corporation | TPU-Polyester | TPUCO® |
| Bio-Flex® F 2201 CL | FKuR Kunststoff GmbH | PLA | Bio-Flex® |
| Bergamid™ BG6600-8057 RS BK001 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Karina IVORY PVC COMPOUND 807D35/ 1-D-AC-LF | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plaslube® PA6/6 CF30 TS12 | Techmer Engineered Solutions | Nylon 66 | Plaslube® |