| HEAT STABILIZED POLYAMIDE 6.6 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 1.1 - 1.8 | % | ASTM D955 |
| -- | 1.1 - 1.8 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 8.5 | % | ASTM D570 |
| Saturated, 23°C | 8.5 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.8 | % | ASTM D570, ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 118 | ASTM D785 | |
| R scale | 118 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 85.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 115 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 60 | J/m | ASTM D256 |
| 23°C | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 205 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 90.0 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 180 | °C | |
| Maximum Continuous Use Temperature | 120 | °C | |
| Melting Temperature | 256 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 120 | kV/mm | IEC 60243-1 |
| Dielectric Constant (1 MHz) | 3.30 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-2 | UL 94 | |
| 3.00 mm | V-2 | UL 94 | |
| Glow Wire Flammability Index | 850 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 270 - 280 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 285 - 310 | °C | |
| Mold Temperature | 65.0 - 110 | °C | |
| Injection Pressure | 70.0 - 125 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 - 85.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBE Polyethylene F022NH | UBE America, Inc. | PE, Unspecified | UBE Polyethylene |
| Fainplast PVC RK 330 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| INELEC PBTCF10 | Infinity LTL Engineered Compounds | PBT | INELEC |
| Kynar Flex® 2950-05 | Arkema | PVDF | Kynar Flex® |
| LNP™ THERMOCOMP™ VF008A compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |