SABIC® PPcompound 108CS20 is a material with good flow, impact and stiffness. The material is part of the SABIC®PP CS systems ans also available as a CS system: using a mixture of 60% SABIC®PP 108MF10 and 40% SABIC®PPcompound 20MBT yields similar properties as listed below. SABIC®PPcompound 108 CS20 is a designated auto grade. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.90 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Injection Molded) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 20.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 17.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | 100 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1500 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 7.0 | kJ/m² | |
| 0°C, Injection Molded | 25 | kJ/m² | |
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 110 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 130 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 7.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® F02-138A | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Sindustris PBT GP2307FY | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| TARFLON™ AK3020 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Sylvin 8240-90 Black 292 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 8200-65 White 1447 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |