BESTNYL SI15VI01BH16
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTNYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tdds2D_BESTNYL-SI15VI01BH16.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6 natural lubrified with 15% glass fibre reinforcement and 25% of mineral charge, heat stabilized is ideal for final applications in the need of good mechanical characteristics and high dimensional stability, generally used in interior pieces in automotive industry. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Water Absorption (23°C, 24 hr) | 0.65 | % | ISO 62 |
| Ash Content | 40 | % | Internal Method |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2 |
| Tensile Stress | 122 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 48 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 200 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | > 220 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 225 to 240 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F850EA (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| TECHNO MUH M3100 | Techno Polymer Co, Ltd. | ABS | TECHNO MUH |
| 4LAC® 25H23100 | 4Plas | ABS | 4LAC® |
| Kepital® F25-03 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |
| Infino WP-1100 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |