YUPLENE® H730F
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SK Global Chemical |
| Trademark: | YUPLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tcUiM8_YUPLENE-H730F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
YUPLENE H730F is propylene homopolymer designed for stretched products such as yarn, tape and rope. YUPLENE H730F complies with FDA regulation 21 CFR177.1520. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ASTM D1238 |
| Spiral Flow | 51.0 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 36.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 500 | % | ASTM D638 |
| Flexural Modulus | 1470 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 49 | J/m | ASTM D256 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Accelerated Oven Aging - in Air (150°C) | 15.0 | day | ASTM D3012 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | 105 | °C | ASTM D648 |
| Vicat Softening Temperature | 152 | °C | ASTM D1525 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| CALIBRE™ 200-15 | Trinseo | PC | CALIBRE™ |
| Clariant Nylon 6/12 612G13-L | Clariant Corporation | Nylon 612 | Clariant Nylon 6/12 |
| Forprene® 6NE001A75 | SO.F.TER. SPA | TPV | Forprene® |
| ELASTOSIL® R 420/40 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Techsil® PU20940 | Techsil Limited | PUR, Unspecified | Techsil® |