Order Products : sales@su-jiao.com
Elastamax™ XL-2065
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Elastamax™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tbDrPD_Elastamax-XL-2065.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PolyOne's Elastamax™ XL thermoplastic olefins (TPOs) are based on pelletized blends of polyolefin resins and select elastomers such EPDM. These materials have been engineered to provide a balance of physical properties and processability, and are an economical alternative to traditional thermoset rubber and more costly thermoplastic elastomers. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.03 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A | 71 | ||
| Shore A, 10 sec | 65 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1 | ASTM D412A | ||
| 100% Strain | 2.69 | MPa | |
| 300% Strain | 3.38 | MPa | |
| Tensile Strength 2(Break) | 6.89 | MPa | ASTM D412A |
| Tensile Elongation 3(Break) | 830 | % | ASTM D412A |
| Tear Strength 4 | 35.9 | kN/m | ASTM D624 |
| Compression Set (23°C, 22 hr) | 35 | % | ASTM D395B |
| Note Message | |
|---|---|
| 1 . | 510 mm/min |
| 2 . | 510 mm/min |
| 3 . | 510 mm/min |
| 4 . | Die C, 510 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mold Max® 27T | Smooth-On, Inc | Silicone | Mold Max® |
| Unilex™ UP.2000.952 | United Polychem | HDPE | Unilex™ |
| Geon™ Vinyl Flexible R291AE | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| EPO-TEK® OG675 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Hapflex™ 871-4 | Hapco Inc. | TP, Unspecified | Hapflex™ |