Kepital® FM2520S
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | taRvpX_Kepital-FM2520S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium viscosity grade for general injection molding. It's modified with MoS2, and so suitable for parts requiring a good friction & wear resistance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.38 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 58.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 33 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | MPa | ISO 178 |
| Flexural Stress (23°C) | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.5 | kJ/m² | ISO 179/1eA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOPAS® 8007D-61 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| Amilan® CM1011G-30 | Toray Resin Company | Nylon 6 | Amilan® |
| Fainplast PVC CTS 01426/1 | Fainplast Compounds S.r.l | PVC Alloy | Fainplast PVC |
| Panlite® ML-7500ZCL | TEIJIN LIMITED | PC | Panlite® |
| Plenco 03303 (Injection) | Plastics Engineering Co. | Phenolic | Plenco |