Ecovio® F2223
| Category: | Copolyester , Copolyester |
| Manufacturer: | BASF Corporation |
| Trademark: | Ecovio® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tZWEAb_Ecovio-F2223.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ecovio® F2223 is our biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester ecoflex ® F Blend and polylactic acid (PLA). Because of the PLA content ecovio ® F2223 consists of 32 % of renewable resources. ecoflex ® F Blend is the continuous phase in the structure of ecovio® F2223 transferring the beneficial film properties of ecoflex® F Blend into the new product. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 to 1.26 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | < 2.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (190°C/5.0 kg) | 3.50 to 7.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 59 | ISO 868 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, Blown Film | 840 | MPa | |
| TD : 50 µm, Blown Film | 280 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 39.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 29.0 | MPa | |
| MD : 50 µm, Blown Film | 39.0 | MPa | |
| TD : 50 µm, Blown Film | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 50 µm, Blown Film | 330 | % | |
| TD : Break, 50 µm, Blown Film | 430 | % | |
| Water Vapor Transmission Rate (50 µm, Blown Film) | 84 | g/m²/24 hr | ASTM F1249 |
| Oxygen Permeability 1 | 670 | cm³/m²/bar/24 hr | ASTM D3985 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Failure Energy - Dyna Test 2(50.0 µm) | 420 | J/cm | DIN 53373 |
| Renewable Content | 32 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ISO 306/A50 |
| Melting Temperature | DSC | ||
| -- 3 | 110 to 120 | °C | |
| -- 4 | 140 to 155 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (50.0 µm, Blown Film) | 85.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| 3 . | ecoflex® |
| 4 . | PLA |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Axiall PVC HHW-191 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| INELEC PE | Infinity LTL Engineered Compounds | HDPE | INELEC |
| Osterlene® PPC-20-NB-200 | Osterman & Company | PP Impact Copolymer | Osterlene® |
| ESTOPLAST XU 64151NN01 | Ester Industries Ltd. | Nylon 66 | ESTOPLAST XU |
| Sylvin 4200-85 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |