| PPE+PS-I Blend with 10% glass fibre; halogen free flame retardant; high heat resistance |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (250°C/21.6 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (23°C, 3.20 mm) | 0.40 - 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | < 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3800 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 82.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 4.0 | % | ISO 527-2/5 |
| Flexural Stress 1(23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m² | ISO 179/1eA |
| 23°C | 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 45 | kJ/m² | ISO 179/1eU |
| 23°C | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 150 | °C | ISO 306/B50 |
| CLTE - Flow (23 to 80°C) | 4.0E-5 - 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.21 | W/m/K | DIN 52612 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 775 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Processing (Melt) Temp | 260 - 300 | °C | |
| Mold Temperature | 60.0 - 100 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 12 - 18 | rpm |
| Injection instructions |
|---|
| Maximum Residence Time: 4 to 10 minInjection Pressure: moderate to high |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Cylinder Zone 1 Temp. | 240 - 270 | °C | |
| Cylinder Zone 2 Temp. | 240 - 270 | °C | |
| Cylinder Zone 3 Temp. | 240 - 270 | °C | |
| Cylinder Zone 4 Temp. | 240 - 270 | °C | |
| Cylinder Zone 5 Temp. | 240 - 270 | °C | |
| Melt Temperature | < 270 | °C |
| Extrusion instructions |
|---|
| Maximum Residence Time: 4 to 10 min |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PE FA3227 | Borealis AG | LDPE | Borealis PE |
| ESTOPLAST EP 4030 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Elastron® G G200.A70.B | Elastron USA, Inc. | SEBS | Elastron® G |
| HiFill® PA4/6 GF45 HS BK | Techmer Engineered Solutions | Nylon 46 | HiFill® |
| SABIC® SUPEER™ 8112L | Saudi Basic Industries Corporation (SABIC) | mLLDPE | SABIC® SUPEER™ |