Miramid® H3KC(U)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Leuna GmbH |
| Trademark: | Miramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tXv3wG_Miramid-H3KC-U-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Miramid® H3KC(U) is a Polyamide 6 (Nylon 6) material. It is available in Europe for injection molding. Important attributes of Miramid® H3KC(U) are:
Typical applications include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1130 | -- | kg/m³ | ISO 1183 1 |
| Water Absorption | ISO 62 2 | |||
| Saturation | 9.0 | -- | % | |
| Equilibrium | 2.5 | -- | % | |
| Viscosity number | 145 | -- | cm³/g | ISO 307, 1157, 1628 3 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | 3400 | 1200 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | 90.0 | 50.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | 4.0 | 20 | % | ISO 527-2 6 |
| Nominal Tensile Strain at Break | 10 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 7 | |||
| -30°C | 4.50 | -- | kJ/m² | |
| 23°C | 5.00 | 20.0 | kJ/m² | |
| Charpy impact strength | ISO 179/1eU 8 | |||
| -30°C | No Break | -- | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 9 | |||
| 0.45 MPa | 190 | -- | °C | |
| 1.8 MPa | 65.0 | -- | °C | |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume resistivity | 1.0E+13 | 1.0E+10 | ohms·m | IEC 60093 10 |
| Dielectric Constant (1 MHz) | 3.40 | 6.00 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.015 | 0.25 | IEC 60250 11 | |
| Comparative tracking index | 600 | -- | IEC 60112 12 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecnoprene® 3T60VB4 NERO900 | SO.F.TER. SPA | PP Copolymer | Tecnoprene® |
| Mowiol® 8-88 low ash | Kuraray Co., Ltd. | PVOH | Mowiol® |
| TYNAB® PM82 | Tyne Plastics LLC. | ABS | TYNAB® |
| Borlink™ LE7710 | Borealis AG | PE, Unspecified | Borlink™ |
| LONGLITE® PBT 6000-280 | CCP Group | PC+PBT | LONGLITE® PBT |