Sindustris ABS LRX821
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tXQHg3_Sindustris-ABS-LRX821.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LRX821 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in the Asia-Pacific region and is processed by extrusion. The main features of Sindustris ABS LRX821 are:
The typical application fields of Sindustris ABS LRX821 are: electrical appliances |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 37 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 38.2 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield, 3.20mm | > 5.0 | % | ASTM D638 |
| Fracture, 3.20mm | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 1860 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 56.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 590 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 290 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 84.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 91.0 | °C | ASTM D1525 5 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Melt Temperature | 200 - 250 | °C | |
| Die Temperature | 200 - 250 | °C | |
| Back Pressure | 0.490 - 0.981 | MPa |
| Extrusion instructions |
|---|
| Mold Temperature: 40 to 80°CScrew Speed: 40 to 82 rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | 15 mm/min |
| 5 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 700.5 | RTP Company | HDPE | RTP |
| RheTech Polypropylene P258-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Cheng Yu T881 | Cheng Yu Plastic Company Limited | PBT | Cheng Yu |
| Fusabond® A560 | DuPont Packaging & Industrial Polymers | EA | Fusabond® |
| LNP™ THERMOCOMP™ RX05494 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |