INEOS EMAA M21N430B

Category:	EMAA , Ethylene Methacrylic Acid
Manufacturer:	INEOS Olefins & Polymers Europe
Trademark:	INEOS EMAA
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	tXLA8f_INEOSEMAAM21N430B.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Ethylene-MethAcrylic-Acid-Copolymer (EMAA) for extrusion coating.

Benefits & Features
M21N430B is an additive free ethylene-methacrylic-acid-copolymer (EMAA) with a low MAA content. Its special polymer structure gives the following properties:

Improved adhesion properties to standard LDPE/mLLDPE or other polar substrates, especially with aluminium foil and metallised film at high line speeds or low coating weights

Good processability in mono- and coextrusion with comparable neck-in and draw down to LDPE

Exhibits good sealing properties enhanced by the presence of the comonomer

Good organoleptical properties

Low fumes during processing, high purity and a low gel level

Applications
M21N430B is a speciality extrusion coating resin with improved adhesion characteristics. Main application fields include aluminium foil and metallized film coating both for industrial use, food and flexible packaging.

General Information
Features	High purity Irritant gas low to no Low speed solidification crystal point Copolymer Workability, good Good sensory characteristics Good heat sealability Good adhesion No additive
Uses	Foil Coatings Packaging Industrial application Food packaging Coating application
RoHS Compliance	Contact manufacturer
Forms	Particle
Processing Method	Co-extrusion molding Extrusion coating

Physical	Nominal Value	Unit	Test Method
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.5	g/10 min	ISO 1133
Methacrylic Acid Content	1.2	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	48		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress			ISO 527-2
Yield, molding	9.00	MPa	ISO 527-2
Fracture, molding	10.5	MPa	ISO 527-2
Tensile Strain (Break, Compression Molded)	500	%	ISO 527-2

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	90.0	°C	ISO 306/A50
Melting Temperature (DSC) ¹	108	°C	Internal method

Extrusion	Nominal Value	Unit
Melt Temperature	260 - 325	°C

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Sylvin 8716-95 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Witcom PPS 6C/3L1-L	Witcom Engineering Plastics B.V.	PPS	Witcom PPS
Durethan® BKV 60 XF 900116	LANXESS GmbH	Nylon 6	Durethan®
LNP™ STAT-KON™ ZE002 compound	SABIC Innovative Plastics Europe	PPE+PS	LNP™ STAT-KON™
TECACOMP® PPA TRM X black 3990	Ensinger GmbH	PPA	TECACOMP®