Staramide P1000IX2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tX3gWE_Staramide-P1000IX2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide P1000IX2 is an Impact Modified Polyamide 6 Injection Molding Resin (also known as P1000HI010 or Star X 2010) |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 1.4 to 1.6 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 55.0 | MPa | |
| Break | 40.0 | MPa | |
| Tensile Strain (Break) | 80 | % | ISO 527-2 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress | 77.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | 85 | kJ/m² | |
| 23°C | > 100 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | 75 | kJ/m² | |
| 23°C | > 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed, 100 mm Span) | 64.0 | °C | ISO 75-2/Ae |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 220 to 230 | °C | |
| Middle Temperature | 230 to 240 | °C | |
| Front Temperature | 240 to 250 | °C | |
| Processing (Melt) Temp | 240 to 250 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 |
| 5 . | 80*10*4 |
| 6 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-G30-(color)-1 | Polymer Resources Ltd. | PC | PRL |
| SABIC® PPcompound 55T1030 | Saudi Basic Industries Corporation (SABIC) | PP Copolymer | SABIC® PPcompound |
| ACCUTECH™ CP0437W10L | ACLO Compounders Inc. | PP Copolymer | ACCUTECH™ |
| LEXAN™ LUX2910T_ resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Innothane® FM-110 | Innovative Polymers, Inc. | TSU | Innothane® |