GELOY™ XTWE265 resin
| Category: | ASA , Acrylonitrile Styrene Acrylate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | GELOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tWePqb_GELOY-XTWE265-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Highly weatherable GELOY ASA profile extrusion grade for processes with simple or no calibration hardware. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.2 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (220°C/5.0 kg) | 5.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.55 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1870 | MPa | ASTM D638 |
| -- | 1900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 38.0 | MPa | ASTM D638 |
| Yield | 37.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 29.0 | MPa | ASTM D638 |
| Fracture | 29.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture 5 | 37 | % | ASTM D638 |
| Fracture | 40 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 1880 | MPa | ASTM D790 |
| -- 7 | 1900 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 53.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 56.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 18 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 260 | J/m | ASTM D256 |
| 23°C 10 | 26 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 35.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 84.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 11 | 75.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 82.0 | °C | ASTM D1525 12 |
| -- | 85.0 | °C | ISO 306/B50 |
| -- | 87.0 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.2E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 1.3E-4 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 87.8 | °C | |
| Drying Time | 3.0 - 6.0 | hr | |
| Cylinder Zone 1 Temp. | 204 - 216 | °C | |
| Cylinder Zone 2 Temp. | 216 - 232 | °C | |
| Cylinder Zone 3 Temp. | 221 - 238 | °C | |
| Cylinder Zone 4 Temp. | 227 - 243 | °C | |
| Adapter Temperature | 227 - 243 | °C | |
| Melt Temperature | 227 - 254 | °C | |
| Die Temperature | 227 - 243 | °C | |
| Calibration Temp, First | 15.6 - 65.6 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 12 hrsMinimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8240-80 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Fainplast PVC GK 91/M | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Fainplast PVC KL 96/5 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| EPO-TEK® B9126-7 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| OxyVinyls® 280 | OxyVinyls, LP | PVC Homopolymer | OxyVinyls® |