Reny® 1032H
| Category: | PARA , Polyarylamide |
| Manufacturer: | Mitsubishi Engineering-Plastics Corp |
| Trademark: | Reny® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tVtTdL_Reny-1032H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reny® 1032H is a Polyarylamide (PARA) material filled with 60% glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Reny® 1032H: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.79 | -- | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 9.4 | -- | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (275°C/2.16 kg) | 5.30 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 0.11 | -- | % | |
| Equilibrium, 23°C, 50% RH | 0.90 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 24700 | 22400 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 249 | 204 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.4 | 1.4 | % | ISO 527-2 |
| Flexural Modulus | 23200 | 21600 | MPa | ISO 178 |
| Flexural Stress | 429 | 357 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | 14 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 54 | 61 | kJ/m² | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 237 | 232 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 230 | 223 | °C | ISO 75-2/A |
| CLTE | ISO 11359-2 | |||
| Flow | 1.0E-5 | -- | cm/cm/°C | |
| Transverse | 4.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 2.0E+14 | 8.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | 2.0E+15 | 8.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | |||
| 1.00 mm | 26 | 26 | kV/mm | |
| 2.00 mm | 20 | 20 | kV/mm | |
| Relative Permittivity | IEC 60250 | |||
| 100 Hz | -- | 6.00 | ||
| 1 MHz | -- | 5.00 | ||
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | -- | 0.020 | ||
| 1 MHz | -- | 0.013 | ||
| Comparative Tracking Index | 550 | > 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 120 | °C | |
| B | 80.0 | °C | |
| Drying Time | |||
| A | > 3.0 | hr | |
| B | > 12 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 275 | °C | |
| Front Temperature | 280 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 20.0 to 150 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Screw Speed | 60 to 150 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X5085 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Manner Flexible PVC C8085 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Shandong PA1212 GYBMVN | Shandong Guangyin New Materials Co., Ltd. | Nylon 1212 | Shandong PA1212 |
| Daelim Po1y® LH210 | DAELIM INDUSTRIAL CO., LTD. | HDPE | Daelim Po1y® |
| Plenco 06582 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |