Versaflex™ HC 2110-57B
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tVcn00_Versaflex-HC-2110-57B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Versaflex™ HC 2110-57B is a TPE designed for use in the healthcare industry offering low stiction and good compression set. New Product. Commercial specifications have not been established.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.01 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.90 - 1.9 | % | ASTM D955 |
| Transverse flow | 1.1 - 2.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shaw A, 10 seconds, 23°C) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain, 23°C | 2.54 | MPa | ASTM D412 |
| 300% strain, 23°C | 3.85 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 3.70 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 350 | % | ASTM D412 |
| Tear Strength | 25.7 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 21°C, 22 hr | 20 | % | ASTM D395B |
| 70°C, 22 hr | 28 | % | ASTM D395B |
| 100°C, 22 hr | 37 | % | ASTM D395B |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 11200 sec^-1) | 9.00 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 166 - 182 | °C | |
| Middle Temperature | 193 - 216 | °C | |
| Front Temperature | 204 - 227 | °C | |
| Nozzle Temperature | 204 - 232 | °C | |
| Mold Temperature | 12.8 - 32.2 | °C | |
| Screw Speed | 80 - 120 | rpm |
| Injection instructions |
|---|
| 在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versaflex™ HC 2110-57B 具有极好的熔体稳定性。最长停留时间可能会根据机筒尺寸有所变化。通常，如果机器闲置 8 - 10 分钟或以上，则应将机筒排空。不需要干燥注射速度：0.5 - 2.5 英寸/秒保持时间（厚部件）：2 - 7 秒保持时间（薄部件）：1 - 3 秒 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP5602 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Kingfa PBT RG20 | Kingfa | PBT | Kingfa PBT |
| LNP™ THERMOCOMP™ WC006 compound | SABIC Innovative Plastics | PBT | LNP™ THERMOCOMP™ |
| SHINSTRA WG25TKB | Shinil Chemical Industry Co., Ltd. | Nylon 66 | SHINSTRA |
| PSM® HL-103 | Wuhan Huali Environmental Technology Co., Ltd. | TP, Unspecified | PSM® |