Menzolit® SMC 1400
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Menzolit Ltd (UK) |
| Trademark: | Menzolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tVBGLi_Menzolit-SMC-1400.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Menzolit® SMC 1400 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor heavy metals. Menzolit® SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The product shows an excellent resistance to common fuels, lubricants, cooling liquids and cleaning materials. Because of its specific matrix resin it is suitable for cyclic loads at higher service temperatures. Typical applications are valve covers, camshaft drive covers, gear box covers as well as oil pans or housings for auxiliary drive systems. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.90 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.030 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (Compression Molded) | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 130 | MPa | ISO 527-2 |
| Tensile Strain (Break, Compression Molded) | 1.6 | % | ISO 527-2 |
| Flexural Modulus (Compression Molded) | 10000 | MPa | ISO 178 |
| Flexural Stress (Compression Molded) | 250 | MPa | ISO 178 |
| Compressive Stress | 140 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | Internal Method | |
| Matrix Crazing Strain | 0.50 | % | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (Compression Molded) | 100 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Continuous Use Temperature | 170 | °C | Internal Method |
| Glass Transition Temperature | 162 | °C | DSC |
| CLTE - Flow | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 135 to 160 | °C | |
| Injection Pressure | 8.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Post Molding Shrinkage |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siloxane Masterbatch MB50-321 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| NuSil MED16-6606 | NuSil Technology | Silicone | NuSil |
| ALTECH® NXT PP-H A 2040/458 GF40 CP | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® NXT PP-H |
| I. Stern 1335 | I. STERN & CO. INC. | PP Homopolymer | I. Stern |
| PLEXIGLAS® Film 0F063 | Evonik Industries AG | Film, PMMA | PLEXIGLAS® Film |