GETILAN ATP/130 XPE
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | GETILAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tUpXg2_GETILAN-ATP-130-XPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Experimental GETILAN ATP/130 XPE: high density chemically crosslinkable polythene for insulated aerial cables. It is a conveniently grafted polythene able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100PSF or MAC/203 HS (red cupper resistant). Adding 5/6% of RESTING HF G 147 the insulation can meetTMX1 Norma. REACTION BETWEEN GRAFTING AND CATALYST: These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 95/5 Certify: HD 626 S1-TMX1 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 1.0 - 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 20.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | 400 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air | IEC 60811 | ||
| 127°C, 40 hr 1 | 7.0 | % | IEC 60811 |
| 150°C, 168 hr 2 | 12 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air | IEC 60811 | ||
| 127°C, 40 hr 3 | -6.0 | % | IEC 60811 |
| 150°C, 168 hr 4 | -16 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset | IEC 60811 | ||
| -- 5 | 0.0 | % | IEC 60811 |
| 150°C 6 | 40 | % | IEC 60811 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | BS 6622 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 190 | °C | |
| Cylinder Zone 4 Temp. | 205 | °C | |
| Cylinder Zone 5 Temp. | 220 | °C | |
| Die Temperature | 225 | °C |
| Extrusion instructions |
|---|
| Crosslinking of the finished product is obtained by: Immersion of the bobbin into hot water at 85/90°C for two hours (up to 3 mm thickness). Steam treatment at 0.15 bar for 5/6 hours. Air crosslinking at natural temperatures and moisture, after a right number of days depending on climatic conditions, is possibile. |
| Note Message | |
|---|---|
| 1 . | Air Bomb |
| 2 . | Heat Aging |
| 3 . | Air Bomb |
| 4 . | Heat Aging |
| 5 . | Residual Value |
| 6 . | 40 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Novomer NB-10 | Novomer, Inc. | PC | Novomer |
| Ecovio® M2351 | BASF Corporation | Copolyester | Ecovio® |
| OmniPro™ CPP TF10 | OMNI Plastics, LLC | PP Copolymer | OmniPro™ |
| SURPASS® HPs667-AB | NOVA Chemicals | HDPE | SURPASS® |
| Sylvin 9067-80 Orange 547 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |