Electrafil® J-50/CF/10
| Category: | PC , Polycarbonate |
| Manufacturer: | Techmer Engineered Solutions |
| Trademark: | Electrafil® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tUkGo8_Electrafil-J-50-CF-10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Electrafil®J-50/CF/10 is a polycarbonate (PC) product, which contains a 10% carbon fiber reinforced material. It can be processed by injection molding and is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Electrafil®The application fields of J-50/CF/10 include packaging, engineering/industrial accessories, automobile industry, commercial/office supplies and conveyor belts. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.15 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 7580 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7580 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 59 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 146 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 142 | °C | ASTM D648 |
| CLTE - Flow | 3.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.5E+5 | ohms | ASTM D257 |
| Volume Resistivity | 5.5E+3 | ohms·cm | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-1 | UL 94 |
| Additional Information |
|---|
| Surface Resistivity, ASTM D257: 1E5-1E6 ohmsVolume Resistivity, ASTM C611: 1E3-1E4 ohm-cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 302 - 316 | °C | |
| Middle Temperature | 316 - 332 | °C | |
| Front Temperature | 310 - 327 | °C | |
| Nozzle Temperature | 310 - 327 | °C | |
| Processing (Melt) Temp | 304 - 327 | °C | |
| Mold Temperature | 71.1 - 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.00 - 0.689 | MPa |
| Injection instructions |
|---|
| Screw Speed: MediumRecommendations for Molding and Tool Conditions: Well vented moldMoisture Content, as received: Product is packaged at 0.2% or less. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LLDPE 118NJ | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |
| Foam-It® 10 SLOW | Smooth-On, Inc | PUR, Unspecified | Foam-It® |
| Karina BLACK PVC COMPOUND 601-48/ 1-BY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYFORM C 27 natural | POLYMA Kunststoff GmbH & Co. KG | Acetal (POM) Homopolymer | POLYFORM |
| TECACOMP® PES PVX black 3777 | Ensinger GmbH | PESU | TECACOMP® |