Toyolac® PX10-X07
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Toray Resin Company |
| Trademark: | Toyolac® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tUFmmN_Toyolac-PX10-X07-79442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toyolac® PX10-X07 is a Polycarbonate + ABS (PC+ABS) product. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.12 | g/cm³ | ASTM D792 |
| 23°C | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (240°C/10.0 kg) | 29 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 114 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| -- | 52.0 | MPa | ASTM D638 |
| 23°C | 57.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 50 | % | ASTM D638 |
| Break, 23°C | 50 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2100 | MPa | ASTM D790 |
| 23°C | 2180 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 79.0 | MPa | ASTM D790 |
| 23°C | 84.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 120 | J/m | |
| 23°C, 3.20 mm | 580 | J/m | |
| 23°C, 12.7 mm | 330 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 6.40 mm | 108 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 115 | °C | |
| CLTE - Flow | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vandar® 2122 | Celanese Corporation | PBT | Vandar® |
| Ferro PP NPP00RS03WH | Ferro Corporation | PP Homopolymer | Ferro PP |
| Gallonprene® GP520-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| KEBAFORM® C 90 W | BARLOG plastics GmbH | Acetal (POM) Copolymer | KEBAFORM® C |
| OTECH ALLOY OM5830-Boot | OTECH Corporation | TP, Unspecified | OTECH ALLOY |