BJB Epoxy TC-1568 A/B
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Epoxy |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tTXOO5_BJB-Epoxy-TC-1568-A-B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TC-1568 A/B is a general-purpose white epoxy surface coat that can be used in conjunction with epoxy resin systems. TC-1568 A/B is noted for its ease of application and its ability to hang on vertical surfaces without sag or runoff. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.63 | g/cm³ | ASTM D792 |
| Specific Gravity | |||
| Part A | 1.726 | g/cm³ | |
| Part B | 1.047 | g/cm³ |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Work Time (25°C) 1 | 30.0 to 35.0 | min |
| Fill Analysis | Nominal Value | Unit | |
|---|---|---|---|
| Brookfield Viscosity | |||
| Mixed : 25°C | Semi-paste | cP | |
| Part A : 25°C | Semi-paste | cP | |
| Part B : 25°C | 2.50 | Pa·s |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 4340 | MPa | ASTM D790 |
| Flexural Strength | 44.8 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 79.4 | °C | |
| 1.8 MPa, Unannealed | 73.9 | °C |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100 | ||
| Part B | Mix Ratio by Weight: 8.0 | ||
| Shelf Life | 52 | wk |
| Note Message | |
|---|---|
| 1 . | 100g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 2020S | Formosa Polypropylene | PP Homopolymer | YUNGSOX® PP |
| DAI-EL™ G-801 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| LTP ZW-3210 | Chengdu Letian Plastics Co., Ltd | Acetal (POM) Copolymer | LTP |
| Pearlthane® 11T65D | Lubrizol Advanced Materials, Inc. | TPU-Capro | Pearlthane® |
| KMI 223L | KMI Group, Inc. | ABS | KMI |