XENOY™ 1102 resin
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | XENOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tSTYGT_XENOY1102resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Unreinforced PC/polyester alloy. Excellent low temperatue impact/chemical resistance to automotive fluids. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792, ISO 1183 |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 13 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 250°C/2.16 kg | 6.00 | cm³/10min | ISO 1133 |
| 250°C/5.0 kg | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.80 - 1.0 | % | Internal method |
| Transverse flow : 3.20mm | 0.80 - 1.0 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 54.0 | MPa | ASTM D638 |
| Yield | 50.0 | MPa | ISO 527-2/50 |
| Fracture | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 4.5 | % | ISO 527-2/50 |
| Fracture 2 | 150 | % | ASTM D638 |
| Fracture | 120 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 3 | 1970 | MPa | ASTM D790 |
| -- 4 | 1880 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 72.0 | MPa | ISO 178 |
| Yield, 50.0mm span 5 | 82.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 6 | 40 | kJ/m² | ISO 179/1eA |
| 0°C 7 | 50 | kJ/m² | ISO 179/1eA |
| 23°C 8 | 55 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 9(-30°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 640 | J/m | ASTM D256 |
| 0°C | 690 | J/m | ASTM D256 |
| 23°C | 800 | J/m | ASTM D256 |
| -30°C 10 | 44 | kJ/m² | ISO 180/1A |
| 0°C 11 | 52 | kJ/m² | ISO 180/1A |
| 23°C 12 | 54 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 110 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 13 | 103 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 6.40mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 14 | 79.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ISO 306/A50 |
| -- | 120 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 50 - 80 | % | |
| Rear Temperature | 243 - 266 | °C | |
| Middle Temperature | 249 - 271 | °C | |
| Front Temperature | 254 - 277 | °C | |
| Nozzle Temperature | 254 - 271 | °C | |
| Processing (Melt) Temp | 260 - 277 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.013 - 0.020 | mm |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*3 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| 14 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 4499 X 83041 | RTP Company | Nylon, Unspecified | RTP |
| Reon 67-01 | Reliance Industries Limited | PVC Homopolymer | Reon |
| Xuchuan XCW-6016HT | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| KEP® KEPA 1150 | Kumho Polychem Co., Ltd. | EPDM | KEP® |
| Kareline® PLMS6040 | Plasthill Oy | PLA | Kareline® |