STERLENE™ BMV203
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | R&P (Pte.) Ltd. |
| Trademark: | STERLENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tRvGAx_STERLENE-BMV203.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| STERLENE™ BMV203 is a compound with high impact designed for automotive exterior painted applications. This product is not UV stabilized. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.01 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 24 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1870 | MPa | ISO 527-2/50 |
| Tensile Stress (Yield, 23°C) | 19.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield, 23°C | 9.3 | % | |
| Break, 23°C | 380 | % | |
| Flexural Modulus 2(23°C) | 1560 | MPa | ISO 178 |
| Flexural Stress 3(23°C) | 26.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/A | ||
| -30°C, Complete Break | 5.6 | kJ/m² | |
| 23°C, Partial Break | 51 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Complete Break | 6.3 | kJ/m² | |
| 23°C, Partial Break | 46 | kJ/m² |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 190 to 240 | °C | |
| Mold Temperature | 25.0 to 60.0 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN504 | RJM International, Inc. | Nylon 6 | RJM |
| Silopren® LSR 4640 | Momentive Performance Materials Inc. | Silicone Rubber, LSR | Silopren® |
| TEKAMID™ TA250G15 | Mando Advanced Materials Co., Ltd. | Nylon 66 | TEKAMID™ |
| CYCOLAC™ INP338 resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |
| PHOENIX™ 4351 | Phon Tech Industrial Company | SEBS | PHOENIX™ |