Nypol® PA A3 D15 TZ CNZ0311 NR388
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tRpnBm_Nypol-PA-A3-D15-TZ-CNZ0311-NR388.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in color gray reinforced with 15% of aluminium silicate, modified the impact, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.19 to 1.21 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 to 0.90 | -- | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.3 | -- | % | ASTM D570 |
| Ash Content | 13 to 17 | -- | % | ASTM D2584 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 110 | 78.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 7.0 | % | ASTM D638 |
| Flexural Modulus | 4600 | 2500 | MPa | ASTM D790 |
| Flexural Strength | 150 | 100 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 60 | 80 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 238 | -- | °C | ASTM D648 |
| Melting Temperature | 250 to 265 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+13 | ohms·cm | ASTM D257 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Prime Cor-X PP with VANISH | Primex Plastics Corporation | PP, Unspecified | Prime Cor-X |
| ALCOM® PBT 700/12 PTFE10 | ALBIS PLASTIC GmbH | PBT | ALCOM® PBT |
| KOPEL® KP3335 | Kolon Plastics, Inc. | TPC-ET | KOPEL® |
| LNP™ STAT-LOY™ LAT4000 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-LOY™ |
| OTECH PVC OW130 - Cable Insulation | OTECH Corporation | PVC, Unspecified | OTECH PVC |