Torelina® A504X90
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | Toray Resin Company |
| Trademark: | Torelina® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tQzeGN_Torelina-A504X90.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Torelina® A504X90 is a Polyphenylene Sulfide (PPS) product filled with 40% glass fiber. It is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Part Marking Code |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.66 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 3.00 mm 1 | 0.80 | % | |
| Flow : 3.00 mm 2 | 0.20 | % | |
| Water Absorption (23°C, 24 hr) | 0.020 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (23°C) | 200 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 1.8 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 15500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 305 | MPa | ISO 178 |
| Shear Strength (23°C) | 80.0 | MPa | JIS K7214 |
| Coefficient of Friction 3 | 0.25 | ||
| Taber Abrasion Resistance (1000 Cycles) | 50.0 | mg | ISO 9352 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 260 | °C | ISO 75-2/A |
| Melting Temperature | 278 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.3E-5 | cm/cm/°C | |
| Transverse | 3.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Electric Strength | 24 | kV/mm | IEC 60243-1 |
| Dielectric Constant 4(23°C, 1 MHz) | 4.20 | IEC 60250 | |
| Dissipation Factor 5(23°C, 1 MHz) | 2.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.280 mm) | V-0 | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bar Flow Length 6(320°C, 1.00 mm) | 135 | mm | Internal Method |
| Note Message | |
|---|---|
| 1 . | 80x80x3 |
| 2 . | 80x80x3mm |
| 3 . | vs. Metal |
| 4 . | 60% RH |
| 5 . | 60% RH |
| 6 . | 98 MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ECO-FLEX™ SA-55A | SYNESIS LLC | RTPV | ECO-FLEX™ |
| Grivory® GV-6 FWA black 9225 | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Karina CLEAR PVC COMPOUND -E 80/278-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Hostacom TRC 352N G22375 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Dow Corning® C6-135 | Dow Corning Corporation | Silicone | Dow Corning® |