TAROLOY 70 is a Polycarbonate + PBT (PC+PBT) product. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 35 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 1.0 to 1.2 | % | |
| Flow | 1.0 to 1.2 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.090 | % | |
| Saturation, 23°C | 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 60.0 | MPa | |
| Break | 55.0 | MPa | |
| Tensile Strain (Break) | > 100 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2100 | MPa | ISO 178 |
| Flexural Stress 2 | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 85.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 3 | 100 | °C | IEC 60216 |
| Vicat Softening Temperature | 180 | °C | ISO 306/A50 |
| Ball Pressure Test (145°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 110 | °C | |
| Pre-heater | 110 to 120 | °C | |
| Drying Time | |||
| -- | 2.0 | hr | |
| Pre-heater | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 1.0 mm/min |
| 3 . | 20000 hrs |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen EP229R | LyondellBasell Industries | Polyolefin, Unspecified | Moplen |
| Generic PPA - Carbon Fiber | Generic | PPA | Generic |
| HAIPLEN H90 TX2 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| LNP™ STAT-KON™ MD000XXZ compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |
| OmniCarb™ PCGF30 | OMNI Plastics, LLC | PC | OmniCarb™ |