WPP PP PRC25UF0C-Black
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Washington Penn Plastic Co. Inc. |
| Trademark: | WPP PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tQFV66_WPP-PP-PRC25UF0C-Black.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
WPP PP PRC25UF0C-Black is a PP Impact Copoly product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. Features include:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.898 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 21.0 | MPa | ASTM D638 |
| Flexural Modulus - Tangent 2 | 900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 83.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 87.8 | °C | |
| Drying Time | 1.0 | hr | |
| Rear Temperature | 218 - 224 | °C | |
| Middle Temperature | 224 - 229 | °C | |
| Front Temperature | 229 - 235 | °C | |
| Nozzle Temperature | 229 - 241 | °C | |
| Mold Temperature | 15.6 - 48.9 | °C | |
| Injection Pressure | 4.14 - 8.96 | MPa | |
| Holding Pressure | 2.41 - 5.17 | MPa | |
| Back Pressure | 0.517 - 1.03 | MPa | |
| Clamp Tonnage | 3.4 - 5.5 | kN/cm² | |
| Cushion | 3.18 - 6.35 | mm |
| Injection instructions |
|---|
| Injection Speed: 1 to 2.5 in/sZone 4 Temperature: 455 to 465°FHot Runner Temperature: 435 to 465°FHydraulic Oil Temperature: 110 to 125°FShot Capacity vs. Barrel Capacity: 2.5 to 4Screw Decompression: 0.1 to 0.25 in |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 31T1010 resin | SABIC Innovative Plastics | PP, Unspecified | SABIC® PPcompound |
| Borealis PP BD712CF | Borealis AG | PP Copolymer | Borealis PP |
| FLEXAREN® 14006 | Innospec Leuna GmbH | EVA | FLEXAREN® |
| INLUBE PA610GF35TF5 | Infinity LTL Engineered Compounds | Nylon 610 | INLUBE |
| Luranyl® KR 2403 G2 TW 26343 | ROMIRA GmbH | PPE+PS | Luranyl® |