Radilon® A 35 990 E GRI
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Radici Plastics |
| Trademark: | Radilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tQAgR3_Radilon-A-35-990-E-GRI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PA66 medium-high viscosity extrusion grade, also suitable for injection moulding. Natural grey colour. Suitable for extrusion processes where medium-high viscosity is required. Also suitable for injection moulding of high thickness parts. Material designed for components requiring low friction coefficient and improved tribological properties. Typical application: cable jacketing. ISO 1043 : PA66 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C, 2.00 mm) | 8.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3300 | 2300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 80.0 | 65.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 5.0 | 20 | % | ISO 527-2/1A/50 |
| Nominal Tensile Strain at Break | 20 | 30 | % | ISO 527-2/1A/50 |
| Flexural Modulus 1 | 2800 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 105 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.5 | -- | kJ/m² | |
| 23°C | 5.5 | 7.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 195 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 90.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 235 | -- | °C | ISO 306/B50 |
| Melting Temperature | 260 | -- | °C | ISO 11357 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | 0.0 | -- | mm/min | FMVSS 302 |
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 80.0 | °C | |
| Drying Time - Desiccant Dryer | 2.0 to 4.0 | hr | |
| Dew Point - Desiccant Dryer | < -20.0 | °C | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Melt Temperature | 270 to 290 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA/PP PA66/PP | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 66+PP | Shandong PA/PP |
| THERMOLAST® K TC3GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Kynar® LBG | Arkema | PVDF | Kynar® |
| LUVOCOM® 1-VAP 10 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| LNP™ LUBRICOMP™ DL004 compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |