ELITE™ 5815P
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tPwWFk_ELITE-5815P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
ELITE™ 5815P is produced via INSITE™ Technology from Dow. It is an ethylene alpha-olefin resin for monolayer and coextrusion coating that offers excellent low temperature seal initiation, ultimate seal strength, hot tack strength and good taste and odor performance.
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.910 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Seal Initiation Temperature 1 | 90.6 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature (DSC) | 124 | °C | Internal method |
| Extrusion | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Temperature | 260 - 316 | °C | |
| Neck-in (316°C, 25.4 µm) | 235.0 | mm | Internal method |
| Minimum coating thickness | µm | Internal method | |
| Minimum coating weight | g/m² | Internal method |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 挤塑机：Black Clawson 螺杆尺寸：3.5 英寸 (90 mm)；30:1 L/D 模具间隙：20 密尔 (0.508 mm) 冷却辊温度：57°F (14°C) 熔体温度：600°F (315°C) 输出：250 磅/小时 气隙：6 英寸 (150 mm) |
| Note Message | |
|---|---|
| 1 . | - Coating onto PET/poly/foil/0.5 mil PRIMACOR- Temperature at which 1 lb/in (4.4 FN/25.4 mm) heat seal strength is achieved.- Heat Seal Strength, Topwave HT Tester, 0.5 S dwell, 40 psi bar pressure, 10 in/min pull speed. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-1950-70A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Telcar® TL-2507B | Teknor Apex Company | TPE | Telcar® |
| Thermovin™ 180 | Vi-Chem Corporation | PVC, Rigid | Thermovin™ |
| WPP PP PPH1CF4-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| Dryflex® PCW 92A331B | ELASTO | TPE | Dryflex® |