MAGNUM™ 3525
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tOBAcK_MAGNUM-3525.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM* 3525 is a resin with excellent processing characteristics. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 11 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2200 | MPa | ISO 527-2 |
| Tensile Stress | |||
| Yield, 3.20 mm, Injection Molded | 43.0 | MPa | ISO 527-2/50 |
| Yield, 3.20 mm, Injection Molded | 44.0 | MPa | ISO 527-2/100 |
| Tensile Strain (Yield, 3.20 mm, Injection Molded) | 3.3 | % | ISO 527-2/50, ISO 527-2/100 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2100 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 11 | kJ/m² | ISO 179/1eA |
| -30°C, Injection Molded | 8.0 | kJ/m² | ISO 179/2C |
| 23°C, Injection Molded | 17 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 12 | kJ/m² | ISO 179/2C |
| Notched Izod Impact Strength | ISO 180/A | ||
| -30°C, Injection Molded | 10 | kJ/m² | |
| 23°C, Injection Molded | 17 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/A | ||
| 1.8 MPa, Unannealed | 78.0 | °C | |
| 1.8 MPa, Annealed | 101 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(2.00 mm) | 60 | mm/min | ISO 3795 |
| Flame Rating 2 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NANCAR® 1204D | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| TPV Elastoprene® N90A-E | ELASTORSA Elastomeros Riojanos S.A. | PP+EPDM | TPV Elastoprene® |
| Generic PS (HIPS) - Glass Fiber | Generic | PS (HIPS) | Generic |
| Geon™ Vinyl Rigid Extrusion L0676 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| OP - PC - Unfilled 46 | Oxford Polymers | PC | OP - PC - Unfilled |