INSPIRE™ TF1500 ESU
| Category: | TPO , Performance Polymers |
| Manufacturer: | Trinseo |
| Trademark: | INSPIRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tNNyzw_INSPIRE-TF1500-ESU.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Talc filled, high impact PP compound. INSPIRE* TF1500 ESU has been developed for aesthetic automotive applications, with good scratch resistance and UV light stabilisation. It is especially suitable for car interior applications requiring ductility, because of its high impact resistance, even at low temperatures. Application areas:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.5 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 to 1.2 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1950 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 20.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Break 1 | 70 | % | ISO 527 |
| Break | 70 | % | ISO 527-2/50 |
| Flexural Modulus | 1850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 5.0 | kJ/m² | |
| 0°C | 10 | kJ/m² | |
| 23°C | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 110 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 58.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/A120 |
| CLTE - Flow | 8.5E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PPX-G15 | Polymer Resources Ltd. | PPE+PS | PRL |
| S&E PVC G-4505 | S&E Specialty Polymers, LLC | PVC, Unspecified | S&E PVC |
| Silmar® SIL95BA-40 | Interplastic Corporation | Polyester, TS | Silmar® |
| SLOVALEN® PC 69 GF 35 FRT 4 | Plastcom | PP, Unspecified | SLOVALEN® |
| Karina IVORY PVC COMPOUND 105770-35/1-CY-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |