Halene L 71602S
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Haldia Petrochemicals Ltd. |
| Trademark: | Halene L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tMQf6d_Halene-L-71602S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
71602S is a LLDPE blown film grade produced by Spherilene Technology. This grade can be used in General Purpose Packaging Film Application. The precise morphological control achieved during polymerization confers excellent processability and mechanical strengths. 71602S is additivated with slip and antiblocking agent for good openability and slip properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 25 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 25 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 25 µm, blown film | 28.0 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 20.0 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 750 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 75 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, blown film | 60 | g | ASTM D1922 |
| TD : 25 µm, blown film | 300 | g | ASTM D1922 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 200 | °C | |
| Cylinder Zone 2 Temp. | 170 - 200 | °C | |
| Cylinder Zone 3 Temp. | 170 - 200 | °C | |
| Cylinder Zone 4 Temp. | 170 - 200 | °C | |
| Cylinder Zone 5 Temp. | 170 - 200 | °C | |
| Melt Temperature | 190 - 200 | °C |
| Extrusion instructions |
|---|
| Blow up Ratio: 2.0-3.0Die Gap: 2.0-2.5 mm |
| Note Message | |
|---|---|
| 1 . | 23°C |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | 38 mm Dart, 66 cm Height |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trexprene® A45NI | Mitsubishi Chemical Performance Polymers, Inc. | TPV | Trexprene® |
| Fixmaster Wear Resistant Putty | Loctite® | Epoxy | Fixmaster |
| Elvax® 3134SBZ | DuPont Packaging & Industrial Polymers | EVA | Elvax® |
| Karina WHITE PVC COMPOUND 809D10/161-BY-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® TPU-8537 | Lehmann & Voss & Co. | PUR, Unspecified | LUVOCOM® |