ELITE™ 5401GS
| Category: | EPE , Enhanced Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | ELITE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tLUB6a_ELITE-5401GS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
5401ELITE™5401GS reinforced polyethylene resin is made of Dow INSITE™The copolymer produced by technology has excellent impact resistance, excellent tear resistance, tensile resistance and optical properties, and can be used to manufacture high-strength blown films. In addition, ELITE™5401GS reinforced polyethylene resin also integrates unique properties such as low initial sealing temperature and high modulus, as well as less blocking, and can be used for automatic packaging. ELITE™5401GS reinforced polyethylene resin contains anti-skid and anti-blocking additives. Purpose:
Compliance:
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.917 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Energy 1(51 µm) | 6.00 | J | ASTM D5748 |
| Film Puncture Force 2(51 µm) | 80.0 | N | ASTM D5748 |
| Tensile Modulus 3 | ISO 527-3 | ||
| 2% secant, MD : 51 µm | 181 | MPa | ISO 527-3 |
| 2% secant, TD : 51 µm | 204 | MPa | ISO 527-3 |
| Tensile Stress 4 | ISO 527-3 | ||
| MD : Yield, 51 µm | 8.00 | MPa | ISO 527-3 |
| TD : Yield, 51 µm | 9.00 | MPa | ISO 527-3 |
| MD : Fracture, 51 µm | 38.0 | MPa | ISO 527-3 |
| TD : Fracture, 51 µm | 37.0 | MPa | ISO 527-3 |
| Tensile Elongation 5 | ISO 527-3 | ||
| MD : Fracture, 51 µm | 570 | % | ISO 527-3 |
| TD : Fracture, 51 µm | 610 | % | ISO 527-3 |
| Dart Drop Impact 6(51 µm) | > 850 | g | ISO 7765-1/B |
| Elmendorf Tear Strength 7 | ASTM D1922 | ||
| MD : 51 µm | 780 | g | ASTM D1922 |
| TD : 51 µm | 980 | g | ASTM D1922 |
| Seal Initiation Temperature 8(51 µm) | 95.0 | °C | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 100 | °C | ASTM D1525 |
| Melting Temperature | 123 | °C | DSC |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 9(45°, 51.0 µm) | 64 | ASTM D2457 | |
| Haze 10(51.0 µm) | 13 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 250 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜挤出的制造条件： 模具间隙：0.8-2.8 mm。 熔体温度：190-250 °C。 放大比：1.5 比 3.5。 |
| Note Message | |
|---|---|
| 1 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 2 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 3 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 4 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 5 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 6 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 7 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 8 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. Achieve a temperature of 5.25 N/15mm heat sealing strength. |
| 9 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| 10 . | Blown film extruded at 232°C, 2.5:1 BUR, 1.8mm mold gap. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MTEGRITY™ LLDPE LL240 | M. Holland Company | LLDPE | MTEGRITY™ LLDPE |
| MOSTEN GB 503 | UNIPETROL RPA | PP Copolymer | MOSTEN |
| 3M™ Dyneon™ PTFE Compound TF 6221 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Borealis PP SC101 | Borealis AG | PP, Unspecified | Borealis PP |
| APICAL 300AF021 | Kaneka Corporation | PI, TS | APICAL |