PRL PPX-GP4-IM
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tKQ9td_PRL-PPX-GP4-IM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PPX-GP4-IM is a Polyphenylene Ether + PS (PPE+PS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/11.6 kg) | 20 to 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 0.50 to 0.70 | % | |
| Across Flow : 3.18 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 34.5 | MPa | |
| Break, 3.18 mm | 34.5 | MPa | |
| Tensile Elongation (Break, 3.18 mm) | 70 | % | ASTM D638 |
| Flexural Modulus (3.18 mm) | 1760 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 48.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 190 | J/m | |
| -18°C, 3.18 mm | 270 | J/m | |
| 23°C, 3.18 mm | 370 | J/m | |
| Gardner Impact (3.18 mm) | 22.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 98.9 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 93.3 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 249 to 299 | °C | |
| Middle Temperature | 260 to 304 | °C | |
| Front Temperature | 271 to 310 | °C | |
| Processing (Melt) Temp | 288 to 316 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Romiloy® 3020/01 M10 | ROMIRA GmbH | ASA+Nylon | Romiloy® |
| Vinylbond 95-950-45 | Colorite Polymers | PVC, Flexible | Vinylbond |
| Clariant Nylon 6/6 PA-133 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Karina IVORY PVC COMPOUND 70900-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Satinice df22 7N | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |