Pearlthane® 11T98
| Category: | TPU-Capro , Thermoplastic Polyurethane Elastomer (Polycaprolactone) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlthane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tIutmI_Pearlthane-11T98.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PEARLTHANE® 11T98 is a polycaprolactone copolyester based TPU, supplied in form of translucent, colourless pellets, combining high hardness with excellent mechanical properties. It can be extruded and injection-moulded. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (20°C) | 1.18 | g/cm³ | ISO 2781 |
| Moisture Content | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 25.0 | mm³ | ISO 4649 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 98 | ISO 868 | |
| Shaw D | 52 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527 | ||
| 100% strain | 16.0 | MPa | ISO 527 |
| 300% strain | 29.0 | MPa | ISO 527 |
| Tensile Stress (Yield) | 40.0 | MPa | ISO 527 |
| Tensile Elongation (Break) | 470 | % | ISO 527 |
| Tear Strength | 180 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395B | ||
| 23°C, 70 hr | 35 | % | ASTM D395B |
| 70°C, 24 hr | 42 | % | ASTM D395B |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature 1 | -30.0 | °C | ISO 11357-2 |
| Melting Temperature 2 | 193 - 203 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Rear Temperature | 195 | °C | |
| Middle Temperature | 205 | °C | |
| Front Temperature | 215 | °C | |
| Nozzle Temperature | 205 | °C | |
| Mold Temperature | 35.0 | °C | |
| Screw L/D Ratio | 23.0:1.0 |
| Injection instructions |
|---|
| Closing force: : 30 tonsScrew diameter: : 26 mmMaximum hydraulic pressure: 210 barMould: : Plaque 120x120x2 mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Cylinder Zone 1 Temp. | 170 - 200 | °C | |
| Cylinder Zone 2 Temp. | 180 - 210 | °C | |
| Cylinder Zone 3 Temp. | 190 - 215 | °C | |
| Cylinder Zone 4 Temp. | 200 - 220 | °C | |
| Die Temperature | 215 - 220 | °C |
| Extrusion instructions |
|---|
| Extruder Speed: 12 to 60 rpmExtrusion Compression Ratio: 2:1 to 3:1Extrusion L/D Ratio: 25:1 to 30:1 |
| Note Message | |
|---|---|
| 1 . | 10°C /min |
| 2 . | Temperature at which MFI = 10 g/10 min @ 21.6 kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2307 A | RTP Company | PUR, Unspecified | RTP |
| STABAMID® 25 RS 4 | Solvay Polyamide & Intermediates | Nylon 66 | STABAMID® |
| Bayblend® FR3006 HF | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Colorite 11 Series 8511 | Colorite Polymers | PVC, Unspecified | Colorite 11 Series |
| POLYCOMPO PE 8200B | POLYCOMPO Co.,Ltd. | HDPE | POLYCOMPO PE |