Anjaflam® 100X-FR/UV
| Category: | PC , Polycarbonate |
| Manufacturer: | Almaak International GmbH |
| Trademark: | Anjaflam® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | tIO9m0_Anjaflam-100X-FR-UV.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Anjaflam® 100X-FR/UV is a Polycarbonate (PC) material. It is available in Europe for injection molding. Important attributes of Anjaflam® 100X-FR/UV are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 11.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.35 | % | |
| Equilibrium, 23°C, 50% RH | 0.15 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 65.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 135 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Glass Transition Temperature | 148 | °C | DSC |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.60 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| 3.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.60 mm | 855 | °C | |
| 2.00 mm | 855 | °C | |
| 3.00 mm | 855 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 5.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 85.0 to 120 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6755 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TEREZ PA 6.6 7530 GF 30 HY | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| NYLEM® 66 GFR 30 FR V0 | EMAS Plastik San.Tic.AS. | Nylon 66 | NYLEM® |
| Elexar® EL-8712R | Teknor Apex Company | TPE | Elexar® |
| XENOY™ 1731 resin | SABIC Innovative Plastics | PC+PBT | XENOY™ |